Lithium batteries are electrochemical devices that are widely used as power sources. This history of their development focuses on the original development of lithium-ion batteries. In particular, we highlight the contributions of Professor Michel Armand related to the electrodes and electrolytes for lithium-ion batteries.
Keywords: intercalation compounds, lithium batteries, electrolyte, cathode, anode
1. Introduction
Lithium “lithion/lithina” was discovered in 1817 by Arfwedson [1] and Berzelius [2] by analyzing petalite ore (LiAlSi4O10), but the element was isolated through the electrolysis of a lithium oxide by Brande and Davy in 1821 [3]. It was only a century later that Lewis [4] began exploring its electrochemical properties. Considering lithium’s excellent physical properties, such as its low density (0.534 g cm−3), high specific capacity (3860 mAh g−1), and low redox potential (−3.04 V vs. SHE), it was quickly realized that lithium could serve well as a battery anode.
In early 1958, Harris [5] examined the solubility of lithium in various non-aqueous (aprotic) electrolytes—including cyclic esters (carbonates, γ-butyrolactone, and γ-valerolactone), molten salts, and inorganic lithium salt (LiClO4)—dissolved in propylene carbonate (PC). He observed the formation of a passivation layer that was capable of preventing a direct chemical reaction between lithium and the electrolyte while still allowing for ionic transport across it, which led to studies on the stability of lithium-ion batteries [5,6]. These studies also increased interest in the commercialization of primary lithium-ion batteries.
Since the late 1960s, non-aqueous 3 V lithium-ion primary batteries have been available in the market with cathodes including lithium sulfur dioxide Li//SO2 in 1969 [7]; lithium–polycarbon monofluoride (Li//(CFx)n commercialized by Matsushita in 1973; lithium–manganese oxide (Li//MnO2) batteries commercialized by Sanyo company in 1975, initially sold in solar rechargeable calculators (Sanyo, Lithium Battery Calculator, Model CS-8176L); lithium–copper oxide (Li//CuO) batteries still used today [8]; and (Li/LiI/Li2PVP) batteries with an Li metal anode, a lithium iodine electrolyte, and a polyphase cathode of polyvinyl-pyridine (PVP) used in cardiac pacemakers since 1972 (see Holmes [9] for the history of this primary battery). Simultaneously, advances in the understanding of the intercalation of lithium in different materials gave birth to rechargeable (secondary) lithium-ion batteries. In this review, we report a brief history of these secondary batteries that have now taken an important place in our daily life, as we find them in many devices ranging from portable phones to electric vehicles. Attention is focused on the beginning of their development in the period of 1970–1990. The contribution of Michel Armand is highlighted in this context.
2. Intercalation Cathode Development
In the early 1970s, research was rekindled in the area of the intercalation reactions of an ion, atom, or molecule into a crystal lattice of a host material without destroying the crystal structure. The following general criteria are needed for reversible intercalation reactions: (a) the materials must be crystalline; (b) there must be empty sites in the host crystal lattice in the form of isolated vacancies or as one-dimensional (1D) channels, 2D layers (van der Waals gap), or channels in a 3D network; and (c) both electronic and ionic conductivity must be present for reversible Li intercalation–deintercalation [10,11]. Based on these criteria, pioneering intercalation studies on Prussian-blue materials, such as iron cyanide bronzes M0.5Fe(CN)3, were demonstrated by Armand et al. [12] in 1972. The same year, the topic of energy storage devices and the concept of solid-solution electrodes and electrolyte components for lithium-based secondary batteries were discussed at a NATO conference in Italy, where Brian Steele suggested the use of transition metal disulfides as intercalation electrode materials [13]. Other groups, notably Gamble et al. [14] and Dines et al. [15,16] (EXXON, USA), evaluated transition-metal chalcogenide (MS2, with M = Ta, Nb, and Ti) electrode materials. At the same conference, Armand suggested the use of several inorganic materials and transition metal oxides, reported the use of CrO3 within graphitic planes as an electrode material for both Li and Na batteries, and described the first solid-state battery using β-alumina as a solid electrolyte [17].
In 1974, inspired by the pioneering work of Rao et al. [18] (IBM, USA) and the group of Rouxel [19] (Nantes, France) who demonstrated the fast kinetics of the intercalation reactions in metal disulfides, Whittingham patented the Li//TiS2 battery [20,21], and the electrochemical properties of Li0//TiS2 battery were simultaneously investigated by Whittingham [22] and Winn et al. [23,24] in 1976. One decade later, Li//TiS2 cells were commercialized under the form of standard-sized XR2016 coin cells by Eveready Battery Co., USA for CMOS memory back-up applications [25,26], under an AA-sized form by Grace Co., USA with a capacity of 1 Ah [27] and under a C-sized form for a cell operating at temperature in the range of −20 to +20 °C with a capacity of 1.6 Ah [28]. Another metal disulfide, namely MoS2, also met success: Li0//MoS2 cells (MOLICELTM) were manufactured by Moli Energy Ltd. in Canada, with an energy density of 60–65 Wh kg−1 at a discharge rate of C/3 (800 mA) [29]. Among other metal chalcogenides investigated at that time, only NbSe3 emerged. Following the study of this material as a cathode element by Murphy et al. [30] in 1976, AT&T (USA) commercialized an AA-sized Li0//NbSe3 cylindrical cell operating over 200 cycles at a current of 400 mA with a capacity of 0.7 Ah in 1989 [31]. For completeness, we mention V2O5, which was also used as a cathode element of commercialized lithium-ion batteries, but this was only done in the 1990s. Since the present review focuses on the early development of lithium batteries, we guide the reader to a book for further details concerning them [32].
Inspired by the studies on NaxCoO2 by the group of Hagenmuller [33] in 1973, Goodenough et al. [34] replaced Na with Li and proposed LiCoO2 as a new cathode (3.9 V vs. Li+/Li) that they patented in 1979. LiCoO2 is more stable in air than NaCoO2, and its good electrochemical properties [35] have earned it the most commercialized cathode for decades. This result opened up a new approach for research into the development of solid-solution materials, in particular Li(NixMnyCoz)O2 (NMC) in the 1990s, as reviewed elsewhere [32].
Early work on spinel LiMn2O4 was carried out in 1984 by Thackeray et al. [36]. Mn is low cost compared to Co, and the thermal stability of LiMn2O4 is better than that of LiCoO2. The problem of Mn’s dissolution into electrolytes at high temperature, however, was not solved until Zhou et al. found an effective salt, LiFNFSI, which improves resilience [37].
Further advances were made in the development of olivine-based cathodes, and in particular LiFePO4, which was pioneered by the Goodenough’s group [38]. The watershed for the use of these materials was the discovery of a carbon-coating process discovered in an international lab (France-Québec) directed by Armand (see Ref. [39] and references therein).
LiFePO4 has a remarkable thermal stability, but its redox potential (3.5 V vs. Li+/Li) is small. LiCoO2 has a rather poor stability, but it belongs to the class of 4 V cathodes. Therefore, in parallel to the development of the LiFePO4 battery, further research was done to improve the thermal stability of LiCoO2 by the synthesis of solid solutions involving doping by Ni, Mn, and non-transition elements. Early work in 1992 by the group of Delmas et al. [40] suggested a solid-solution concept that was then explored by many groups to optimize the Li(NixMnyCoz)O2 (NMC) cathode that is now commercialized by various companies due to its high energy density; it now shares the market with LiFePO4.
3. Development of Anode Materials
In addition to the development of positive (cathode) electrode materials, research was also carried out on Li-metal and Li-alloy negative (anode) electrodes. Early batteries were commercialized with such anodes [25,26,27,28,29,30,31]. However, they faced safety concerns due to the formation of anode dendrites.
The insertion of lithium in graphite dates from 1955, but this was only confirmed by the synthesis of LiC6 in 1965 [41]. The synthesis of LiC6, however, was not obtained by electrochemical process at that time, and the reversible intercalation of lithium in graphite up to LiC6 was established by Besenhard and Eichinger in 1976 [42,43], but, owing to a lack of a suitable electrolyte that could prevent co-intercalation at that time, graphite was not used as a cathode material. This problem was solved by the group of Armand in 1978 by the use of polymer electrolyte that allowed these authors to identify the suitability of graphite as an intercalated negative electrode [44,45].
In the 1970s, Armand proposed the fabrication of a lithium-ion battery based on two different intercalation materials for both cathodes and anodes; this battery was named the rocking-chair battery (later the lithium-ion battery) due to the shuttle of ions from one electrode to another during the charge–discharge process [46]. This concept involved lithium ions being transferred from one side to the other [45] and was demonstrated in 1980 by Lazzari and Scrosati [47].
The rocking-chair battery concept was thus offered the same year as the LiCoO2 positive electrode was proposed by Goodenough, but the laboratory experiment has to be taken to the industrial scale. This was achieved by the commercialization of the LiCoO2//hard-carbon battery by the Sony and Asahi Kasei teams led by Nishi in 1991. The rocking-chair concept later gained major success in the Japanese battery industry with Sony [48] (1985) and Sanyo in 1988 [49].
In the 1990s, another anode material, the spinel Li4Ti5O12, was proposed for Li-ion batteries [50,51] and, more recently, for Na-ion batteries [52]. This anode may substitute graphite only when high-power density is needed, but in Na-ion batteries, the Li4Ti5O12 electrode delivers a reversible capacity of 155 mAh g−1 and presents the best cycle ability among all reported oxide-based anode materials [53].
4. Electrolytes
Armand was a pioneer in the development of a polymer electrolytes based on polyethylene oxide-lithium salts (PEO:Li) [54,55]. Solid-state batteries have the advantage that they use Li as the anode the collector current. As a result, the theoretical energy density of solid-state batteries is larger than that of Li-ion batteries that use liquid electrolytes. The drawback is that the PEO and polymers in general have a poor ionic conductivity at room temperature, so that the commercial all-solid-state lithium-ion batteries that use polymers, such as the batteries in Bluecars® and Bluebuses®, must be used at elevated temperatures. On another hand, liquid electrolytes are very good ionic conductors, and it is difficult to avoid the formation of dendrites at the surface of lithium metal. As a consequence, liquid electrolytes have been adopted in commercial batteries. Such is the case, for instance, for the above-mentioned LiCoO2 battery of Sony that used LiPF6 in propylene carbonate and diethyl carbonate (PC:DEC, 1:1) as the electrolyte. However, PC and DEC are not compatible with lithium metal, so Li-ion batteries with liquid electrolytes adopt the rocking-chair concept with graphite anodes proposed by Armand, implying a smaller theoretical energy density but a higher rate capability at room temperature than all-solid-state batteries. The use of graphite, however, implies that PC was commonly used in the first batteries, as its intercalation results in exfoliation of the carbon sheets. Indeed, the Sony LiCoO2-type battery used hard carbon as the anode. The long cycle life of Li-ion batteries with graphitic carbon and liquid electrolytes (without PC) was demonstrated by Basu [56] in 1981, who used a two-molar solution of LiAsF6 dissolved in 1,3 dioxolane. Only in the 1990s, however, did commercialized batteries emerge with a graphite anode using a liquid electrolyte with LiPF6 in carbonate solvents; this is still the standard today.
In 1991, the group of Armand reported a novel salt: lithium bis(trifluoromethanesulfonyl)imide (LiTFSI) [57], now commonly used as an Li-ion conducting electrolytes for Li-ion batteries and later on a new class of single-ion solid polymer [58,59] and solvent-in-salt electrolytes [60], which gives more evidence that Armand was one of the researchers that played a major role in the development of lithium-ion batteries in the period of time covered in this review. Actually, the period of time where he played a major role is continuing. Further details, including the more recent contributions of Armand to the field of electrolytes, were discussed in a recent review [46], but his recent contributions include advanced materials in all components, including electrodes, of lithium- and sodium-ion batteries [61,62].
Prior patents that paved the route to the present Li-ion batteries are reported in Table 1, and the increase of the energy density of the batteries through the early years of rechargeable batteries is illustrated in Table 2. Note, however, that this figure can only give a partial view of the progress since energy density is not the only parameter that is meaningful. For instance, a battery with an LiFePO4 cathode and a Li4Ti5O12 anode can be cycled over 30,000 cycles at very fast rate of 15C (4 min) and a discharge rate of 5C (12 min) [63]. This performance gives interest to such a battery for some applications, even though its energy density is smaller than that of the LiFePO4-graphite battery, since the operating voltage of the battery is reduced by 1.5 V.